Vandan Steel & Engg. co. is one of the trustworthy and prominent exporter and supplier of SA 516 GR.60 plates that are comprehensively used in a total extent of organizations on account of its unimaginable mechanical properties and features. This assessment of plates is available in a combination of sizes, shapes, structures, and points of interest recollecting the necessities of customers.
Being an assumed association, we are totally busy with giving all of our customers splendid thing not in the private country yet in various countries too. The plates are used in a wide extent of usages both in the mechanical and business region.
We, before giving these A516 GR.60 Steel plates to the customers, guarantee that all of the things are without disfigurement and offer the best execution under the specific domains of working. These plates are generally used in weight vessels as they can easily oversee high temperature and weight without getting hurt.
The steel assessment is used for moderate to cut down temperature working and is used for the formation of weldable business and present day steel weight vessels and boilers. It is on a very basic level institutionalized steel that is known for its weldability and sublime indent toughness. It is basically used in the pressurized organizations in petrochemical and oil and gas industry.
Before amassing these steel plates, there are two principal techniques done as such as to make the rough steel into high gauge and useable structure that is (BF) or basic oxygen radiator and (EAF) or an electric bend warmer. These two methods help in making high gauge of steel which can be used for making steel plates. Close by this, these plates are encircled using high gauge of rough material that is purchased from the strong market merchants. The rough material is particularly evaluated and attempted by the quality examiners that guarantee every material is of high bore and will give its best under the individual domains of working
|Supply Condition||As Rolled, Normalized Rolling, Furnace Normalizing, Vacuum Degassing, Simulated Post-Weld Heat Treatment or as per customer requirement|
|Impact tested||-52° C|
|Tempering||Notch toughness can be improved by quenched cooling from hot rolling or normalizing by the supplier. If such a faster cooling rate is agreed upon between purchaser and supplier then the steel is also to be tempered at 1200 F.|
|Applications||Used for weld fabrication of pressure vessels that require improved notch toughness for lower than ambient temperature service.|
|Grade||British Standard||European Norm||ASTM/ASME||DIN|
|Gr. 60||BS1501-161-430A||EN10028 P265GH||A/SA516 – Grade 60||DIN 17155 HII|
|Grade||Tensile strength||Yield strength||Elongation min, %|
|Gr. 60||415-550 Mpa||250 Mpa||21|