These High MANGANESE 12-14 % PLATES are non-alluring in nature. They are the austenitic sort of steel. This steel is especially sensible for the 'were' application. In these applications, there is the necessity for high influence scratched spot or there is a prerequisite for gouging scratched region which may incite a work cementing sway. The manganese steel plates can end up being hard when the outside of the plate is again and again going up against impact or scratched spot. This steel is having progressively conspicuous toughness which is the gotten feature from the high unbending nature contained by it. It is in like manner especially bendable in nature and it furthermore engages the paralyze prompts be held safely.
Vandan Steel & Engg. co. are providers of Manganese Steel Plates and Sheets to revelation X120Mn12 and 1.3401. As a high manganese steel grade it offers bewildering work setting properties. 12 - 14% Manganese Steel Plates and Sheets ends up being perpetually hard when the surfaces of parts are in peril to rehashed impact or scratched spot. Its quality, got from high flexibility and congeniality, pulls in amaze prompts be acclimatized safely.
The plates are scratched zone safe a stunning metal work High quality explanation behind constrainment. Ideal for wearing plates for continuing with structure, this manganese steel evaluations are totally referenced in various affiliations.
This high manganese assessment is an astounding mix making, scratched spot safe steel. This manganese steel is a non overwhelming austenitic sort, gave in full Plates or as profiled pieces by plasma cutting. Reasonable for wear applications where high sway/gouging scratched zone prompts a work setting effect.High manganese steel Plates winds up being truly hard when the surfaces of regions are made game plans to included impact or scratched zone. Its quality, got from high undaunted nature and versatility, interfaces with stupor prompts be drained securely.
These manganese steel assessment plates are viewed as staggering for the setting up and scratched zone work. The manganese steel plates are everything considered called non-interfacing with austenitic steel plates that are given to various endeavors as plasma cutting. These plates are viewed as reasonable for wear endeavors and applications where the high effect scratched zone work is finished. These plates become dependably hard when the outside of the plates is more than once affected.
|Elements||C (%)||Mn (%)||Si (%)||S (%)||P (%)|
|ASTM 128 Gr B2||1.05 – 1.2||11.5 – 14||< 1.0||—||<0.070|
|Manganese||1.13 – 1.2||11.5 – 14||<0.40||<0.003||<0.020|
|YIELD||TENSILE UTS 20° C (68° F)||ELONGATION||CHARPY Kcvl 20°C (4°F)||HARDNESS BHN|
|350 MPa 51 KSI||940 MPa 136 KSI||(5d) 40%||>140J/cm2 100 ft. lbs||220 to 540|
|Density *||Expansion Coeff.
|7.88||10 ⁻⁶ °C ⁻¹
10 ⁻⁶°F ⁻¹
|J/Metric Kg. °C